Adhesives, Compounds, Sealants
GLUES «КДС 600», «КДС 600-1» (Technical conditions «АДИ» 529-2002)
The adhesives under brand «КДС 600», «КДС 600-1» intended for gluing metal and non-metallic materials, (including steel, ceramics, concrete, metal, fibro-metals in various combinations and working at a temperature of -60 to +120 C.
The adhesives are simple to use, stands to vibration and thermal loads, durable, have high level of water- oil-petrol-resistance , environmentally safe. One of the main advantages of the adhesives developed is a possibility of their use in damp environments and wet agents, as well as in conditions of high-pressure filtration and temperature from +4ºC .
Physical and mechanical properties:
Name of indicators |
КДС - 600 |
КДС- 600-1 |
|
Visual appearance |
A viscous mass, black |
A viscous mass, brown |
Viability from the date of preparation, at a temperature (20+1)°C, min |
Not less than 15 |
Not less than 60 |
Density, g/cm3 |
Not less than 1,5 |
Not less than 1,5 |
Ultimate tensile Stress, MPa |
Not less than 10,0 |
Not less than 10,0 |
Ultimate shearing Strength, MPa |
Not less than 60,0 |
Not less than 60,0 |
COMPOUNDS «КДС -174», «КДС-174-1» (Technical conditions «АДИ» 542-02)
Compounds under brand «КДС -174», «КДС-174-1» , relate to gluing metallic and nonmetallic materials and paint products radio electronics industry, working in a wide range of vibration and thermal loads. Compound curing at a temperature of the workshop when in contact pressure within 24 hours. Compounds are oil-petrol-resistant.
Permissible to use compound for gluing products in the water.
The number of components - 2
Physical and mechanical properties:
Visual appearance |
Low-viscous mass of dark-color |
Ultimate shearing strength on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 13,0 |
Ultimate tension on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 15,0 |
Percentage of breaking elongation % |
6 |
Density, g/cm3 |
1,05 |
Operating free-air temperature range, ° C |
-60 ...…..+150?С |
HYPPERTHERMAL GLUE «ВТК-1Х» (Technical conditions «АДИ» 447-94)
Phenolic cement is used to connect parts of graphite, ceramics and composite materials based on carbon, working in high-heat area of products in the inert environment or reducing zone at temperatures up to 2000 º C. The number of components - 4 The regime curing: cold, 20 º C - 48 hours, or 20 º C hot - 24 hours, then 80 º C - 3 hours
Physical and mechanical properties:
Visual appearance |
Homogeneous pasty mass of black |
Viability in the range temperature 15 - 35 ° C, min |
Not less than 120 |
Ultimate tensile strength on test pieces “steel-steel” , MPa |
|
at a temperature of 20 ?С |
14,4 |
at a temperature of 50?С |
14,4 |
at a temperature of 300?С |
5,4 |
Ultimate homogeneous tension on test pieces “steel-graphite” , MPa |
|
at a temperature of 20?С |
8,9 |
at a temperature of 50?С |
8,1 |
at a temperature of 300?С |
3,4 |
Ultimate homogeneous tension on test pieces “graphite-graphite” , MPa |
|
at a temperature of 20? |
3,3 |
at a temperature of 300?С |
1,9 |
at a temperature of 500?С |
3,4 |
at a temperature of 1000?С |
2,5 |
at a temperature of 1500?С |
4,8 |
at a temperature of 1700?С |
3,7 |
POTTING COMPOUND «КДС-25» (Technical conditions «АДИ» 426-93)
Binary cold curing compound under brand «КДС-25», intended for the manufacture of models for casting, standard models for pouring R&E applications, working at a temperature of: -60 to +120 C.
Physical and mechanical properties:
Visual appearance |
Homogeneous mass without extraneous inclusions, bright shades |
Density, g/cm3 |
1,05 |
Ultimate tension, MPa |
40,0 |
Ultimate crushing strength, MPa |
70,0 |
Percentage of breaking elongation % |
3,3 |
The vitality, min |
60 |
Ultimate tensile strength, MPa |
15,0 |
Per-unit volume electric resistance, ohm*cm |
2,1012 |
Dielectric strength, kV/mm |
14,0 |
REPAIR COMPOSITE SHS-17
Repair composite is intended for luting cracks in pipelines with hot and cold water, gas and oil pipelines. Widely used for stopping pores and blowholes in nonferrous castings, as well as, a variety works of repair and rehabilitation of worn surfaces.
Intervals operating temperatures :
from -60 to +120 º C.
The regime curing:
Cold - 15-35 º C - 48 hours
Hot - 15-35 º C - 2-10 h, then 60-80 º C - 5-7 h
Physical and mechanical properties:
Visual appearance |
Homogeneous highly mass of darkgrey color |
Viability in the range temperature 15 - 35 ° C, min |
Not less than 60 |
Ultimate tensile strength on test pieces “steel-steel” , MPa |
Not less than 5,0 |
GLUES «КДС-15» and «КДС-15-1»(Technical conditions 2252-001-31949494-2004)
Cold curing Clay «КДС-15» is intended for gluing metal and non-metallic materials in various combinations. Functional in a temperature of -60 º C to +150 º C. Clay «КДС-15-1» is an analog of glue «ПУ-2».
Clay is curing at a temperature of the workshop with a contact pressure within 72 hours.
The number of components - 3.
Physical and mechanical properties:
Visual appearance |
Низковязкая масса темного цвета |
Ultimate shearing strength on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 20,0 |
Ultimate tension on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 20,0 |
Percentage of breaking elongation at 20 ° C,% |
3,0 |
Density, g/cm3 |
1,05 |
Operating free-air temperature range, ° C |
-60……..+150?С |
COMPOUND «ЗЛК -11»
Pouring cold curing compound is for filling electronic products industry, working in a wide range of vibration and thermal loads. Compound curing at a temperature of the workshop with a contact pressure within 24 hours.
Physical and mechanical properties:
Visual appearance |
Homogeneous light mass |
Viability in the range temperature 15 - 35 ° C, min |
Not less than 60 |
Ultimate shearing strength on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 4,0 |
Ultimate tension on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 4,0 |
Percentage of breaking elongation at 20 ° C,% |
Not less than 30,0 |
Density, g/cm3 |
1,2 |
POTTING COMPOSITION «КДС-23-2» (Technical conditions «АДИ» 554-2004)
Epoxy organic silicon composition is intended for curing cold gluing metal and non-metallic materials, has high adhesion and kogesion durability, resistance to action vibrating loads, thermal and hydraulic strikes, work at the temperature range from -196 to 300 º C. Pillars to the effects of water, oil, gasoline and diesel fuel, pillars in alkaline and acidic environment.
Composition is curing at a temperature of the workshop with a contact pressure within 72 hours.
The number of components - 3
Physical and mechanical properties:
Ultimate tension on glued connections done with steel «Ст.3» at the temperature range, not less than, MPa |
|
at 20? С |
12 |
at 200? С |
2,0 |
at 300?С |
0,5 |
Ultimate tension on glued connections done with steel «Ст.3» in 7 days of cure, at 20 ° C of the temperature, in hydraulic oil Environment not less than, MPa |
|
at 20? С |
12 |
at 100? С |
2,0 |