Adhesives, Compounds, Sealants
GLUE «КДС-17» (Technical conditions «АДИ 215-85»)
Clay is for curing cold gluing metal and non-metallic materials, working in conditions of heat and vibration loads.
Clay is curing at a temperature of the workshop with a contact pressure within 24 hours.
Physical and mechanical properties:
Visual appearance: |
Homogeneous viscous mass of grey color |
Viability in the range temperature 15 - 35 ° C min |
Not less than 60 |
Ultimate shearing strength at 20 ° C, MPa |
Not less than 10.0 |
Ultimate tension at 20 ° C, MPa |
Not less than 11.0 |
Percentage of breaking elongation at 20 ° C,% |
Not less than 3.0 |
Density, g/cm3 |
0,8 |
Operating free-air temperature range, ° C |
- 40°… + 150 ° C |
Resistant to the effects of alkalis, acids, water, alcohol mixtures airwaves, all types of fuels and other inorganic and organic solvents.
GLUE «ЭКАН-3» (Technical conditions «АДИ 381-91»)
Epoxy-elastic cold curing clay is designed for gluing metal and non-metallic materials (including steel, rubber, rubber-polyamide, glass, rubber) in various combinations and working at a temperature from -60° to +150 ° C.
The number of components - 2
Profiles: the
Cold, 20 ° S - 24 hours,
Hot 20 ° C - 2 hours, then 60° - 80° C - 3-4 h.
Physical and mechanical properties:
Visual appearance |
Homogeneous viscous mass of dark purple color |
Viability in the range temperature 15 - 35 ° C, min |
Not less than 60 |
Percentage of breaking elongation at 20 ° C, after 24 h % |
40 |
Percentage of breaking elongation, after thermostatting at 20 ° C during 7 h |
30 |
Ultimate tensile strength on test pieces “steel-steel” , MPa |
|
at a temperature of -10 ° C |
17,3 |
at a temperature of 20 ° C |
13,7 |
at a temperature of 60 ° C |
4,9 |
Ultimate tensile stress on rubber-covered test pieces “steel-steel”, coated with rubber «ИРП-2021» & fiberglass plastic «ППН-100»,MPa |
|
at a temperature of -10 ° C |
6,6 |
at a temperature of 20 ° C |
4,4 |
at a temperature of 60 ° C |
2,9 |
GLUE «КДС-19» (Technical conditions «АДИ 344-90»)
Clay is for curing cold gluing metal and non-metal- lic materials, working in a wide range of the vibration and firing rates.
Clay curing at a temperature of the workshop with a contact pressure within 24 hours.
Physical and mechanical properties:
Visual appearance |
Homogeneous viscous mass of dark red color |
Viability in the range temperature 15 - 35 ° C min |
Not less than 60 |
Ultimate shearing strength at 20 ° C, MPa |
Not less than 15,0 |
Ultimate tension at 20 ° C, MPa |
Not less than 17,0 |
Percentage of breaking elongation at 20 ° C,% |
Not less than 12,0 |
Density, g/cm3 |
1,1 |
Operating free-air temperature range, ° C |
-50.….+150?С |
Resistant to the effects of alkalis, acids, water, mixture of alcohol, ether and other inorganic and organic solvents.
COMPOUND «ЗЛК-15» (Technical conditions «АДИ 214-85 »)
Potting cold curing compound is for sealing electronic products industry, working in a wide range of vibration and firing rates.
Compound is curing at a temperature of the workshop with a contact pressure within 24 hours.
Physical and mechanical properties:
Visual appearance |
Homogeneous white liquid |
Viability in the range temperature 15 - 35 ° C min |
Not less than 60 |
Ultimate shearing strength on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 4,0 |
Ultimate tension on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 6,0 |
Percentage of breaking elongation at 20 ° C,% |
Not less than 30,0 |
Density, g/cm3 |
0,95 |
Per-unit volume electric resistance, ohm*cm |
4*109 |
Tangent of the dielectric losses angle |
0,05 |
Dielectric permeability |
3,8 |
Electric strength, kV / mm |
8,0 |
Operating free-air temperature range, ° C |
- 60.... +150?С |
COMPOUND «ЗЛК-17» (Technical conditions 2257-002-31949494-2004)
Potting cold curing compound is done for sealing in electronic products industry, working in a wide range of vibration and firing rates.
Compound curing at a temperature of the workshop with a contact pressure within 24 hours.
Physical and mechanical properties:
Visual appearance |
Homogeneous transparent liquid |
Viability in the range temperature 15 - 35 ° C min |
Not less than 60 |
Ultimate shearing strength on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 4,0 |
Ultimate tension on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 6,0 |
Percentage of breaking elongation at 20 ° C,% |
Not less than 40,0 |
Per-unit volume electric resistance, ohm*cm |
4*10 10 |
Tangent of the dielectric losses angle |
0,05 |
Dielectric permeability |
3,8 |
Electric strength, kV / mm |
20,0 |
Operating free-air temperature range, ° C |
- 60.... +150?С |
THERMAL-RESSISTANT GLUE «ТКС-500» (Technical conditions «АДИ 495-2000»)
Epoxy organic silicon clay is a cold curing adhesive designed for gluing metal and non-metallic materials, has high adhesion and cohesion durability, resistance to action of vibrating, thermal and hydraulic strikes, working at the range of temperatures - 196 to 300 º C, briefly up to 500 º C. Proof to the effects of water, oil, gasoline and diesel fuel.
Clay curing at a temperature of the workshop with a contact pressure within 72 hours.
The number of components - 3
Physical and mechanical properties:
Visual appearance |
Homogeneous viscous mass of brown color |
Viability in the range temperature 15 - 35 ° C min |
Not less than 60 |
Percentage of breaking elongation after 24 h, % |
10 |
Ultimate tension on glued connections done with steel «Ст.3» at the temperature range, not less than, MPa |
|
at 20 ?С |
18 |
at 300 ?С |
0,8 |
PETROL PROOF GLUE «КДС-23» (Technical conditions «АДИ 505-2000»)
Epoxy organic silicon clay cold curing adhesive is designed for gluing metal and non-metallic material, has high adhesion and cohesion durability, resistance to action vibrating loads, thermal and hydraulic strikes, work on the temperature range from -196 to 300 º C. Pillars to the effects of water, oil, gasoline and diesel fuel, pillars in alkaline and acid environment. Clay curing at a temperature of the workshop with a contact pressure within 72 hours.
The number of components - 3
Physical and mechanical properties:
Ultimate tension on glued connections done with steel «Ст.3» at the temperature range, not less than, MPa |
|
at 20? С |
12 |
at 200? С |
2,0 |
at 300?С |
0,5 |
Ultimate tension on glued connections done with steel «Ст.3» in 7 days of cure, at the temperature range, not less than, MPa |
|
at 20? С |
12 |
at 100? С |
2,0 |
GLUE «КВС» -31 «В3-80-89»
Clay is for curing cold gluing metal and non-metallic materials in various combinations.
Functional in a temperature of -60 to +150 º C
Drying regimes :
Cold, 20 º C - 24 h,
Hot 20 º C - 2 hours, then 60 .... 80 º C - 3-4 h.
Physical and mechanical properties:
Visual appearance |
Homogeneous viscous mass of dark purple color |
|
Viability in the range temperature 15 - 35 ° C, min |
60 |
|
Percentage of breaking elongation at 20 ° C, after 24 h % |
40 |
|
Percentage of breaking elongation, after thermostatting at 20 ° C during 7 h |
30 |
|
Ultimate tensile stress on test pieces “steel-steel” , MPa |
||
at a temperature of -10 ° C |
17,3 |
|
at a temperature of 20 ° C |
13,7 |
|
at a temperature of 60 ° C |
4,9 |
|
Ultimate tensile stress on rubber-covered test pieces “steel-steel”, coated with rubber «ИРП-2021» & fiberglass plastic «ППН-100»,MPa |
||
at a temperature of -10 ° C |
6,6 |
|
at a temperature of 20 ° C |
4,4 |
|
at a temperature of 60 ° C |
2,9 |
|
COMPOUND «ЗЛК-19П»(Technical conditions «АДИ 430-95»)
Potting cold curing compound is for sealing in electronic products industry, working in a wide range of vibration and firing rates Compound curing at a temperature of the shop with a contact pressure within 24 hours.
Maximum lot of mixing components - 1 kg.
Physical and mechanical properties:
Visual appearance |
Homogeneous white liquid |
Viability in the range temperature 15 - 35 ° C min |
Not less than 40 |
Ultimate shearing strength on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 5,0 |
Ultimate tension at 20 ° C, MPa |
Not less than 5,0 |
Density, g/cm3 |
0,5 |
Per-unit volume electric resistance, ohm*cm |
2*10 |
Tangent of the dielectric losses angle |
0,05 |
Dielectric permeability |
4 |
Dilectric strength, kV / mm |
4,6 |
Operating free-air temperature range, ° C |
-60 ..….+150?С |
COMPOUNDS «КДС -173-1», «КДС-173-2» (Technical conditions «АДИ» 490-2000)
Compounds under brand «KDC -173-1», «КДС-173-2 KDS» intended for repair concrete structures long operated in the aquatic environment. The use of compound reduces the volume of water filtration by 85% and increase the service life of concrete structures in 1,2-1,5 times.
Compound curing at a temperature from 4 º C.
Compounds are oil, gasoline, water -resistant.
Physical and mechanical properties:
Visual appearance |
Viscous mass of black and brown colors |
Viability in the range temperature 4° C, min |
Not less than 60 |
Ultimate shearing strength on glued connections done with carbon steel at 20 ° C, MPa |
Not less than 10,0 |
Percentage of breaking elongation at 20 ° C,% |
12,0 |
Density, g/cm3 |
1,50 |
Operating free-air temperature range, ° C |
-60 ..….+150 ?С |
Continuation of section "Adhesives, Compounds, Sealants"